3M 1300L
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Brush or Spray Application
- High Immediate Strength and Heat Resistance
- Metal, Rubber, and Wood Bonding
Product Description
3M™ Neoprene High Performance Rubber & Gasket Adhesive 1300L is a versatile, polychloroprene-based adhesive designed for bonding rubber and gasket materials. As a lower-solids and lower-viscosity version of 3M Adhesive 1300, it offers easier brushing and sprayability while providing high immediate strength and excellent heat resistance. It effectively bonds neoprene, SBR, and butyl rubber to metal, wood, and most plastics.
Key features
- Broad temperature resistance: Maintains performance across a wide temperature range from -34°C to 149°C.
- Fast bonding range: Offers a short bonding range of up to 8 minutes for efficient assembly.
- Industry compliant: Meets the specification requirements of MMM-A-121.
Applications / Suitable for
- Bonding neoprene, SBR, and butyl rubber
- Adhering rubber to metal, wood, and most plastics[
- General gasket and rubber assembly
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Thermal Properties
Mechanical Properties
Additional Information
As-supplied / before-processing properties
Typical properties; these values are not intended for use in preparing specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Base | Polychloroprene | - | - |
| Color | Yellow | - | - |
| Solids Content by Weight | 26-33 | % | - |
| Viscosity | 250-1000 | cP | at 27°C (80°F) |
| Flash Point | -26 | °C | Closed Cup |
After-processing / final-state properties
Typical properties; these values are not intended for use in preparing specifications.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| 180° Peel Adhesion | 768 | oz/in | Canvas to Steel, 72 h at 23°C (73°F) |
| Overlap Shear Strength | 343 | lb/in² | Birch to Birch, 2 week cure, tested at -34°C (-30°F) |
| Overlap Shear Strength | 549 | lb/in² | Birch to Birch, 2 week cure, tested at 66°C (150°F) |