LOCTITE ABLESTIK 2114
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Optically Clear Bonding
- 50 N/mm^2 Cured Tensile Strength
- Broad Metal/Glass/Ceramic/Plastic Compatibility
Product Description
LOCTITE ABLESTIK 2114 BIPAX is a two-component, transparent, non-conductive epoxy adhesive supplied in a BIPAX mixing-dispenser package for easy mixing. Formulated for optical clarity and low viscosity, it is recommended for industrial adhesive and laminating applications. This solvent-based system cures at room temperature over 24 hours or with an accelerated schedule, and supports continuous service from -60°C to 110°C. It bonds metals, glass, glass fabrics, ceramics, and plastics, offering strong tensile strength, good electrical insulation, and environmental and chemical resistance in its cured state.
Key features
- Transparent with optical clarity: Low viscosity and refractive index of 1.57 for optically clear bonding applications.
- High tensile strength: 50 N/mm² (7,200 psi) tensile strength in the cured state.
- Electrically insulating: Dielectric strength of 410 volts/mil supports non-conductive assembly needs.
Applications / Suitable for: Industrial adhesive and laminating applications across metals, glass, glass fabrics, ceramics, and plastics.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Electrical Properties
Additional Information
As-supplied / before-processing properties
Typical properties of the uncured, mixed material prior to cure.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Viscosity, mixed | 640 | mPa·s (cP) | @ 25°C, mixed |
| Specific gravity, mixed | 1.17 | — | Mixed material |
| Pot life | 60 | minutes | Mixed material |
After-processing / final-state properties
Typical properties of the fully cured material after the recommended cure schedule.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Hardness | 78 | Shore D | Cured material |
| Glass transition temperature (Tg) | 77.0 | °C | Cured material |
| Dielectric strength | 410 | volts/mil | Cured material |
| Tensile strength | 50 (7,200) | N/mm² (psi) | Cured material |
| Lap shear strength, Al to Al | 16.2 (2,350) | N/mm² (psi) | Sample cured 1 hr @ 100°C |