BONDERITE S-FN GP 1904
Harmonization Code : 3403.19 | Lubricating Preparations (With 70% or More Petroleum Oils) For Automotive and Other Uses
Main features
- PTFE/Graphite Dry-Film Lubricant
- Corrosion and Solvent Resistance
- Multi-Substrate Dry Lubrication
Product Description
BONDERITE® S-FN GP 1904 ACHESON is a one-package resin-bonded dry film lubricant formulated with PTFE and graphite in a thermosetting binder. It is designed for spray, brush, or dip application to produce a durable, low-friction coating with excellent corrosion and solvent resistance. Its broad curing temperature range allows use on engineering metals as well as wood, rubber, and many plastics. :contentReference[oaicite:0]{index=0}
Key Features
- PTFE and graphite dry film lubricant providing low-friction performance.
- Excellent corrosion and solvent resistance after curing.
- One-package formulation suitable for spray, brush, or dip application.
- Wide curing temperature range for compatibility with metals, wood, rubber, and many plastics.
- Flexible coating with consistent spray and dip-spin application characteristics.
Applications / Suitable for
- Fasteners
- Sliding rails
- Lock mechanisms
- Seat belt components
- Latches
- Mechanical assemblies
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Product TypeProduct Type
PTFE/graphite dry-film lubricantAdditional Information
Technical Properties
As-Supplied / Before-Processing Properties
| Property | Value | Unit | Method / Condition |
|---|---|---|---|
| Technology | Dry film lubricant | — | Supplier classification |
| Pigment | PTFE and graphite | — | Wet product |
| Binder | Thermoset | — | Wet product |
| Appearance | Black liquid | — | Wet product / SDS |
| Carrier | MEK or BONDERITE L-FG SB-2 ACHESON | — | Supplier description |
| Viscosity | 100 | mPa·s (cP minimum) | Typical |
| Density / Specific Gravity | 0.96 (0.959 SDS) | kg/L | Typical |
| Solids content | 25 | % by weight | Typical |
| Flash point | 8°C (TDS); 7.78°C closed cup (SDS) | °C | Typical |
| VOC | 720 | g/L | Typical |
| Recommended storage temperature | 5–30 | °C | SDS |
| Shelf life | Not stated | — | Refer to product label or TDS |
Technical Properties
After-Processing / Final-State Properties
| Property | Value | Unit | Method / Condition |
|---|---|---|---|
| Coating color | Black | — | Cured coating |
| Coefficient of friction | 0.08–0.10 | — | Static |
| Recommended dry film thickness | 0.008–0.025 | mm | 0.0003–0.0010 in |
| Theoretical coverage | 6.81 | m²/kg | @ 25 µm dry film thickness |
| Continuous service temperature | 149 | °C | 300°F |
| Salt spray resistance | >96 | hours | ASTM B117 over zinc phosphated surface, 25 µm coating |
| Typical curing schedules | 149°C / 60 min; 177°C / 10 min; 204°C / 8 min | — | Substrate temperature |