LOCTITE 411
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- High-Viscosity Cyanoacrylate Gel
- Controlled Non-Sag Application
- High Peel Strength
Product Description
LOCTITE® 411™ is a one-component, high-viscosity ethyl cyanoacrylate adhesive gel designed for gap-filling applications involving rubbers, plastics and metals. The adhesive combines excellent peel strength with enhanced heat resistance while maintaining the rapid curing characteristics typical of cyanoacrylates. Its gel consistency prevents migration after application, allowing precise placement on vertical and irregular surfaces. LOCTITE 411 cures rapidly in the presence of atmospheric moisture and develops strong bonds across a wide range of substrates, making it suitable for industrial assembly, repair and maintenance applications.
Key Features & Benefits
- High-viscosity gel formulation with gap-filling capability.
- Excellent peel strength compared with standard instant adhesives.
- Enhanced heat resistance for demanding environments.
- One-component adhesive requiring no mixing.
- Fast humidity-activated cure at room temperature.
- Suitable for bonding rubbers, plastics and metals.
- Controlled non-sag application on vertical surfaces.
Recommended Applications
- Gap-filling bonding applications.
- Rubber-to-metal and plastic-to-metal assemblies.
- General industrial assembly and maintenance.
- Applications requiring improved peel strength.
- Elevated-temperature bonding environments.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Additional Information
As-Supplied / Before-Processing Properties
| Property | Value | Unit | Condition |
|---|---|---|---|
| Technology | Cyanoacrylate | — | Ethyl cyanoacrylate gel adhesive |
| Chemical Type | Ethyl Cyanoacrylate | — | High-strength instant adhesive |
| Appearance | Water White to Slightly Cloudy Gel | — | Uncured |
| Components | One Part | — | No mixing required |
| Specific Gravity | 1.05 | — | 25°C |
| Brookfield Viscosity | 4,000 - 8,000 | mPa·s (cP) | RVT, Spindle TC, 20 rpm, 25°C |
| Key Substrates | Rubbers, Plastics and Metals | — | Typical bonding materials |
| Cure Type | Humidity Cure | — | Atmospheric moisture activated |
After-Processing / Final-State Properties
| Property | Value | Unit | Condition / Method |
|---|---|---|---|
| Glass Transition Temperature (Tg) | 120 | °C | ASTM E228 |
| Coefficient of Thermal Expansion | 80 × 10⁻⁶ | K⁻¹ | ISO 11359-2 |
| Thermal Conductivity | 0.1 | W/m·K | ISO 8302 |
| Volume Resistivity | 10 × 10¹⁵ | Ω·cm | IEC 60093 |
| Dielectric Breakdown Strength | 25 | kV/mm | IEC 60243-1 |
| Lap Shear Strength (Steel, Grit Blasted) | 18 - 26 | N/mm² | ISO 4587, 24 h @ 22°C |
| Lap Shear Strength (Aluminum, Etched) | 11 - 19 | N/mm² | ISO 4587, 24 h @ 22°C |
| Lap Shear Strength (ABS) | >6 | N/mm² | ISO 4587, 24 h @ 22°C |
| Tensile Strength (Steel) | 12 - 25 | N/mm² | ISO 6922, 24 h @ 22°C |
| Tensile Strength (Buna‑N) | ≥7.0 | N/mm² | ISO 6922, 30 s @ 22°C |
| Lap Shear Strength at 121°C | ≥8.3 | N/mm² | After 24 h @ 22°C + 24 h @ 121°C |