Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Medium-Viscosity Application Control
- Rubber-to-Wood Epoxy Bonding
- Chemically, Environmentally and Temperature Resistant
Product Description
LORD® 305-1/305-2 Epoxy Adhesive is a general-purpose, medium-viscosity, two-component epoxy adhesive designed to produce strong, durable, chemically and environmentally resistant structural bonds. It provides excellent adhesion to prepared metals, fiberglass reinforced plastics (FRP), phenolics, wood, prepared rubber and other engineering materials. The adhesive is also suitable for bonding cured rubber to itself and rubber to metal, including gaskets, bushings, shock-absorbing devices and rubber rolls. LORD® 305 can be cured at room temperature or heat cured to accelerate production while delivering reliable performance across a service temperature range of -30°F to +250°F (-34°C to +121°C). :contentReference[oaicite:0]{index=0}
Key Features
- Medium-viscosity, two-component epoxy adhesive for durable structural bonding.
- Excellent adhesion to metals, FRP, phenolics, wood, prepared rubber and other engineering substrates.
- Resists moisture, sunlight, weathering, dilute acids, alkalis, solvents, greases and oils while providing low shrinkage and good creep resistance.
Applications / Suitable For
- General structural bonding applications
- Metal and composite assemblies
- Bonding cured rubber to itself or to metal components
- Gaskets, bushings, shock-absorbing devices and rubber rolls
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Additional Information
As-Supplied / Before-Processing Properties
| Property | 305-1 Resin | 305-2 Hardener | Method / Condition |
|---|---|---|---|
| Appearance | Clear amber liquid | Blue liquid | Typical |
| Viscosity | 10,000–18,000 cP | 20,000–45,000 cP | Brookfield HBF, Spindle 2, 10 rpm, 77°F (25°C) |
| Density | 9.4–10.0 lb/gal (1126–1198 kg/m³) | 7.75–8.35 lb/gal (928–1001 kg/m³) | Typical |
| Flash Point | >200°F (>93°C) | >200°F (>93°C) | Closed Cup |
| General Purpose Mix Ratio | 1:1 by volume (1.2:1 by weight) | -30°F to +250°F (-34°C to +121°C) | |
| Solids Content | 100% | Mixed adhesive | |
| Working Time | 1–2 hours | 75°F (24°C), 54 g mass | |
| Time to Handling Strength | 8–16 hours | Typical | |
| Mixed Appearance | Blue liquid | Typical | |
| Shelf Life | 2 years | Stored unopened at 60–80°F (16–27°C) | |
After-Processing / Final-State Properties
| Property | Value | Method / Condition |
|---|---|---|
| Cure Schedule | 24–48 hours | 65°F (18°C) or higher |
| Service Temperature | -30°F to +250°F (-34°C to +121°C) | Typical operating range |
| Tensile Strength at Break | 3350 psi (23.1 MPa) | ASTM D638 |
| Elongation | 9.9% | ASTM D638 |
| Young's Modulus | 283,694 psi (1956 MPa) | ASTM D638 |
| Glass Transition Temperature (Tg) | 141°F (61°C) | ASTM E1640-99 by DMA |
| Cured Appearance | Translucent Blue | Typical |