LORD 410/19GB
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- Glass-Bead Bondline Control
- 20-30 Minute Working Time
- Non-Sag Vertical Application
Product Description
LORD 410 / 19GB Acrylic Adhesive System is a two-component structural bonding system combining LORD 410 acrylic adhesive with Accelerator 19GB. The non-sag paste bonds prepared or minimally prepared metals and engineered plastics, including polycarbonate, ABS, acrylics, and XENOY, with a 20 to 30 minute working time at 24 deg C. Accelerator 19GB contains glass beads for controlled bondline thickness, while the mixed system reaches handling strength in 60 to 120 minutes and full cure in 24 hours at room temperature. The service-temperature range is -40 to 149 deg C.
Key features
- Glass-Bead Bondline Control: Accelerator 19GB contains glass beads for controlled adhesive thickness.
- 20-30 Minute Working Time: Provides a defined assembly window at 24 deg C.
- Non-Sag Structural Bonding: Remains in position on vertical and overhead surfaces.
Applications / Suitable for
- Structural bonding of prepared or minimally prepared metals.
- Bonding engineered plastics including polycarbonate, ABS, acrylics, and XENOY.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Thermal Properties
Physical Properties
Additional Information
Adhesive and accelerator properties
Values apply to LORD 410 adhesive with LORD Accelerator 19GB and are typical unless noted.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| LORD 410 appearance | Off-white to tan paste | As supplied; typical | |
| LORD 410 viscosity | 100,000 to 300,000 | mPa s | 25 deg C, Brookfield; typical |
| LORD 410 density | 9.15 to 9.65 | lb/gal | As supplied; typical |
| LORD 410 flash point | 15 | deg C | Typical |
| Mix ratio | 4:1 | by volume | LORD 410 adhesive : Accelerator 19GB |
| Mix ratio | 2.91:1 | by weight | LORD 410 adhesive : Accelerator 19GB |
| Solids content | 100 | % | Mixed with recommended accelerator; typical |
| Mixed appearance | Tan paste | LORD 410 with Accelerator 19GB; typical |
Mixed-system and cure properties
Values apply to the LORD 410 / Accelerator 19GB system; cured mechanical data for other accelerator combinations are not included.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Working time | 20 to 30 | min | 24 deg C; typical |
| Handling-strength time | 60 to 120 | min | 24 deg C, 60 psi shear criterion; typical |
| Full-cure time | 24 | h | 24 deg C; typical |
| Cured appearance | Tan to green | LORD 410 with Accelerator 19GB; typical | |
| Service-temperature range | -40 to 149 | deg C | Adhesive-system range |