ROYAL DOUBLE BUBBLE 04001
Harmonization Code : 3214.10.00 | Putty and other mastics | Resin cements, caulking compounds and other mastics
Main features
- Fast 15-to-30-Minute Handling
- Premeasured 1:1 Packet Mixing
- High-Cohesion Structural Repair
Product Description
Hardman Double/Bubble 04001 Extra Fast-Set Epoxy is a 3.5 g premeasured, two-part epoxy packet for fast structural bonding, fixturing, patching, and repair. The amber liquid mixes at 1:1 by volume and has a 3 to 5 minute gel time at 25 deg C, followed by 15 to 30 minute handling time and full cure in 24 hours at 23 deg C. Typical cured data include 3,000 psi overlap shear strength on acid-etched aluminum at 25 deg C and 80 Shore D hardness. The grade bonds metals, wood, concrete, ceramics, stone, glass, leather, and many plastics.
Key features
- Premeasured 1:1 packet: The 3.5 g dual pouch keeps the two components portioned for one-shot mixing.
- Fast handling: Handling strength develops in 15 to 30 minutes at room temperature.
- Cured structural strength: Typical overlap shear strength is 3,000 psi on acid-etched aluminum at 25 deg C.
Applications
Applications include fast bonding, patching, fixturing, and repair of metal, ceramics, glass, wood, concrete, stone, leather, and selected plastics.
TDS, SDS & Technical Documents
Technical Specifications
Thermal Properties
Additional Information
As supplied / before processing
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Package size | 3.5 | g | Premeasured dual-pouch packet |
| Volume mix ratio | 1:1 | - | Part A to Part B |
| Mixed viscosity | 40,000 | cP | At 25 deg C |
| Gel time | 3-5 | min | At 25 deg C; 4 g mixed mass |
| Handling time | 15-30 | min | Room-temperature cure |
| Full cure | 24 | h | At 23 deg C |
After processing / final state
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Hardness | 80 | Shore D | ASTM D2240 |
| Tensile strength | 7,250 | psi | ASTM D638 |
| Elongation at break | 8.5 | % | ASTM D638 |
| Overlap shear strength | 3,000 | psi | Acid-etched aluminum; ASTM D1002; 25 deg C and 50% RH |
| T-peel strength | 1.8 | pli | Acid-etched aluminum-to-aluminum; 25 deg C |
| Operating temperature | 82 | deg C | Cured adhesive |