AEROWAX HT
Harmonization Code : 3208.20.90 | Paints and varnishes that are dispersed or dissolved in a non aqueous medium
Main features
- 82 to 88 deg C Melting Range
- Chemical-Resistant Selective-Plating Maskant
- UV-Detectable BIOACT-Removable Coating
Product Description
AEROWAX™ HT Wax Maskant is a highly refined platers wax for selective plating operations. Supplied in slab form, it has a melting-point range of 82–88°C (180–190°F) and is used to mask both simple and complex part geometries during hard chrome, nickel sulfamate, and other selective plating processes. The wax combines adhesion and flexibility with resistance to crazing, cracking, elevated process temperatures, and harsh plating chemicals. It is detectable under UV light for inspection and can be removed using Petroferm BIOACT® 280 series dewaxing agents. One-tank and two-tank dip processes are documented, with a minimum of two wax coats recommended.
Key features
- Selective-plating maskant for simple and complex geometries.
- High-temperature wax with an 82–88°C (180–190°F) melting-point range.
- Adhesive and flexible coating that resists crazing and cracking.
- Resistant to harsh plating chemicals under the intended process conditions.
- UV detectable to support inspection of the applied wax mask.
- Removable with Petroferm BIOACT® 280 series dewaxing agents.
Applications / Suitable for
- Hard chrome selective plating.
- Nickel sulfamate selective plating.
- Other selective plating operations requiring a removable wax maskant.
Technical Specifications
No specifications available.
Additional Information
AEROWAX™ HT Wax Maskant
A highly refined platers wax for masking simple and complex part geometries during hard chrome, nickel sulfamate, and other selective plating operations. The wax combines adhesion and flexibility with high-temperature stability, chemical resistance, UV detectability, and removal using compatible BIOACT® dewaxing agents.
As-supplied properties
Typical property data are provided for product evaluation and are not specification limits.
| Property | Typical value | Context |
|---|---|---|
| Form | Slabs | As supplied |
| Melting-point range | 82–88°C (180–190°F) | Typical |
| Needle penetration | Approximately 18 dmm | At 25°C |
| Kinematic viscosity | 16.5–21 mm²/s | At 100°C |
Masking process
Add AEROWAX™ HT to the tank reservoir and apply heat. Use clean, dry parts and apply a minimum of two wax coats. Build the coating through repeated dipping until the required mask thickness is reached.
Wax removal
After plating, remove AEROWAX™ HT using Petroferm BIOACT® 280 series dewaxing agents. Establish the removal process for the part geometry, wax thickness, and applicable cleaning conditions, and follow the current cleaning-agent instructions and safety documentation.
AEROWAX™ HT is available in 60 lb (27 kg) cartons. Shelf life is 36 months when stored in the original sealed container above 10°C (50°F). Consult the current Safety Data Sheet for handling and disposal requirements.
Applications
AEROWAX™ HT is used as a removable mask during selective plating. Final process suitability depends on part cleanliness, geometry, wax thickness, bath conditions, plating chemistry, and dewaxing requirements.
Evaluate AEROWAX™ HT for your selective plating process
Contact Krayden to discuss part geometry, tank configuration, wax temperature, coating build, plating chemistry, UV inspection, removal using BIOACT® dewaxing agents, packaging availability, and process trials.