ARALDITE TDR 1100-11
Harmonization Code : 8529.90 | Parts solely or principally used for TV, radio, and transmission
Main features
- Glass, Plastic, and Wood Bonding
- 2:1 Meter-Mix Processing
- 90-Minute Working Window
Product Description
TDR 1100-11 is a thixotropic, two-part epoxy adhesive specifically formulated for bonding glass laminate, wood, and plastic components. Designed primarily for use in the construction of archery bows, this system features a convenient 2:1 by volume mix ratio that is well-suited for automated metering equipment.
Key features
- Extended working time: Features a long pot life of over 90 minutes to accommodate complex assembly processes.
- Accelerated processing: Cures quickly at temperatures above 170°F (77°C) to help streamline production.
- Aesthetic finish: Formulated to produce a clear bond line, preserving the visual quality of the final assembly.
Applications / Suitable for
- Formulated for the construction of archery bows.
- Bonding glass laminate components.
- Bonding wood and plastic materials.
Technical Specifications
General Properties
Mix RatioMix Ratio
2:1Pot LifePot Life
95 minutesMechanical Properties
ElongationElongation
3.6% to 4.6% (depending on cure schedule) %Additional Information
Technical properties
As-supplied / before-processing properties
Pre-cure physical and processing characteristics of TDR 1100-11.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Mix Ratio (Volume) | 2:1 | - | Resin to Hardener |
| Mix Ratio (Weight) | 100:42 | - | Resin to Hardener |
| Viscosity (Mixed System) | 13,000 | cP | ASTM D2393 |
| Pot Life | 95 | minutes | 4 fl oz, ASTM D2471 |
Technical properties
After-processing / final-state properties
Cured mechanical properties of TDR 1100-11 when cured for 15 minutes at 180°F (82°C).
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Ultimate Strength | 9,100 (62.7) | psi (MPa) | Cure: 15 min at 180°F (82°C) |
| Lap Shear Strength (at 77°F) | 3,520 (24.3) | psi (MPa) | Cure: 15 min at 180°F (82°C) |
| Modulus of Elasticity | 396,000 (2,731) | psi (MPa) | Cure: 15 min at 180°F (82°C) |
| Heat Deflection Temperature | 164 (73) | °F (°C) | Cure: 15 min at 180°F (82°C) |